Activated carbon organic adsorption capacity and continued development
CLM: Activated carbon organic adsorption capacity and continued development
Activated carbon organic adsorption capacity and continued development
23 Sep 2021 in 04:46am
Physical method is to use carbon dioxide, water vapor or the mixture of both as activator, the carbonized carbon material and gas in the activation furnace at 500~1200℃ for carbon activation reaction, so that the pore size of the carbonized material to expand, the formation of activated carbon with porous microcrystalline structure.Gas activation method mainly includes carbonization and activation engineering.The so-called carbonization, refers to the low temperature (about 500℃) is small, the volatile coal tar molecules in the material and the thermal decomposition and curing process of asphalt, that is, to remove the volatile in advance, made suitable for the next step of activation with carbonization.
When the temperature is below 600℃, the specific surface area of carbonized material increases with the increase of temperature.When 600~900℃, the specific surface area reaches a certain value: 250~300 m2/g; when above1000℃, the specific surface area shrinks rapidly.
When the carbonization temperature is above 800℃, the reaction performance of carbonized compounds and activation gas gradually becomes weaker, so the carbonization temperature is generally below 1000℃. However, if the residual volatile content and thermal effect are taken into account, the most suitable temperature should be 600~700℃39].
The carbonized substance obtained from the carbonization process is placed in water vapor or a mixture of water vapor and combustion gas and heat treated at 800~1000℃, which is called the activation process.activated carbon pellet wholesaleactivated carbon manufacturers in china
When the temperature is below 600℃, the specific surface area of carbonized material increases with the increase of temperature.When 600~900℃, the specific surface area reaches a certain value: 250~300 m2/g; when above1000℃, the specific surface area shrinks rapidly.
When the carbonization temperature is above 800℃, the reaction performance of carbonized compounds and activation gas gradually becomes weaker, so the carbonization temperature is generally below 1000℃. However, if the residual volatile content and thermal effect are taken into account, the most suitable temperature should be 600~700℃39].
The carbonized substance obtained from the carbonization process is placed in water vapor or a mixture of water vapor and combustion gas and heat treated at 800~1000℃, which is called the activation process.activated carbon pellet wholesaleactivated carbon manufacturers in china